BACK

COMMODITY: W02 ALLOY
NO: W02
DESCRIPTION:
WO2 (Nickel-containing)
APPLY: Nickel-platinum, 14k, 18k (750) - Machine Cast
Ingredients of 1000grams 18k Platinum alloy:
750 grams granular pure gold
250grams W02
1.Please prepare a new ceramic crucible, and a new ceramic or stone gold stirring rod, use new products in order to avoid contamination of residues of the last operation
2.All metal must be completely dry before fed into the crucible melting
3.Melting formula: Calculate the target per 1000 grams
4.Melt 750grams of pure gold in 1100℃
5.Piece 250 grams of W02 slowly when the pure gold melted to liquid. Do not add all W02 on once, because if it is done so, the temperature of the liquid metal will be immediately decreased, and then cured. Once cured, it is difficult to melt. Make sure all W02 operation are absorbed completely.
6.Fully stirred. Stirring rod must be first heating before contact with the liquefied metal.
7.Mold。The temperature should be within 1050 and 1120, which is relevant with mold equipment and material.
8.Quench for 20-45 minutes after casting. Detect every cold quenching cycle, wrong timing will make it too soft or too hard.
9.Extended into sheet or filamentous. Use the box-shaped extended furnace if you can. Keep metal set for 20 minutes at 720 degrees heating zone. Make sure the metal red disappears before take the metal away from heating zone and cold quenching in water. Do not quench in water directly.

 

PRE

NEXT

 

 

 

 
     

6F., No.2-1, Aly. 195, Yongfong Rd., Tucheng Dist., New Taipei City 236, Taiwan (R.O.C.)

TEL:+886-2-2260-1555  FAX:+886-2-2265-0922  WEB: www.superspark.com.tw  

SUPER SPARK INTERNATIONAL CO.,LTD (c)2013 All Rights Reserved.